WitrynaIn this work, the permeability of carbon dioxide through Nafion® EW 1100 has been studied at different temperatures, ranging from 30 to 80 °C. Three conditions were … Witrynafonate groups. The structure of Nafion in the protonated form is shown in Fig. 1. For Nafion 1100, the equivalent weight is 1100 g/mol, which is consis-tent with polymer …
Ionic conductivity of an extruded Nafion 1100 EW series of …
Witryna19 lut 2016 · Small-angle scattering experiments (SAXS/SANS) have shown the radius of cylindrical water channels to be 5–20 % smaller in extruded than in solution-cast hydrated Nafion of 1100 g EW. 7c, 16 It follows that the circumference of an idealized, cylindrical channel (as well as the channel surface area) is accordingly 5–20 % larger for N212 ... WitrynaFor more than 50 years, Nafion™ membranes and dispersions have provided critical applications with unparalleled performance and durability. Today, the Nafion™ … tegenungan wasserfall bali
Xion™ PEM-Nafion-1100-10 - fuelcellstore.com
Witrynaprobe experiments. Samples equilibrated under 0% relative humidity still contained approximately one water per sulfonate, (ì) 1). These samples will be referred to as “dry” Nafion. All samples prepared in the humidity system were sealed in sample cells between 3 mm thick CaF2 windows and separated by a 200 ím Teflon spacer. The … WitrynaIonic Conductivity of an Extruded Nafion 1100 EW Series of Membranes ... vapor,13,16-19,23,26-28and humidified gases30,31 at temperatures from 20 to 95°C. WitrynaIonic Conductivity of an Extruded Nafion 1100 EW Series of Membranes tegepang ba dada